    • Comparing intergranular corrosion in Al‐Mg‐Si‐Cu alloys with and without α‐Al(Fe,Mn,Cu)Si particles 

      Lervik, Adrian; Danbolt, Turid; Furu, Trond; Holmestad, Randi; Lunder, Otto (Peer reviewed; Journal article, 2020)
      In this study, a model alloy without Fe and Mn additions, is compared with a commercial AA6005 alloy to further understand how the α‐Al(Fe,Mn,Cu)Si particles affect intergranular corrosion (IGC) behaviour. Both alloys were ...

    • Corrosion performance of different alloys exposed to HTL conditions – a screening study 

      Bengtsson Blucher, Daniel; Lange, Torstein; Sandquist, Judit; Saanum, Inge; Uusitalo, Mikko (Peer reviewed; Journal article, 2024)
      The corrosion and material evaluation study in (a) water-based simulated black liquor and (b) water-based simulated black liquor at super-critical conditions was successful. The conclusion from the testing program was that ...

    • Corrosion performance of different alloys exposed to HTL conditions – a screening study 

      Bengtsson Blucher, Daniel; Lange, Torstein; Sandquist, Judit; Saanum, Inge; Uusitalo, Mikko (Peer reviewed; Journal article, 2024)
      The corrosion and material evaluation study in (a) water-based simulated black liquor and (b) water-based simulated black liquor at super-critical conditions was successful. The conclusion from the testing program was that ...

    • Root causes for corrosion on painted steel structures in marine environments 

      Knudsen, Ole Øystein; Hagen, Catalina Hoem Musinoi; Skilbred, Anders Werner Bredvei; Bruaas, Tarjei K.; Nærland, Jarand (Peer reviewed; Journal article, 2023)
      Our understanding of the failure mechanisms of coatings, for example, cathodic disbonding, corrosion creep, blistering, and cracking, have been developed to a high level over the past decades. However, knowing what actually ...