Effect of Heat Treatment on the Ductility of Inconel 718 Processed by Laser Powder Bed Fusion
Peer reviewed, Journal article
Accepted version
Permanent lenke
https://hdl.handle.net/11250/2685105Utgivelsesdato
2020Metadata
Vis full innførselSamlinger
- Publikasjoner fra CRIStin - SINTEF AS [5865]
- SINTEF Industri [1571]
Originalversjon
International Workshop of Advanced Manufacturing and Automation (IWAMA) 2019: Advanced Manufacturing and Automation IX 10.1007/978-981-15-2341-0_13Sammendrag
Inconel 718 is a precipitation-hardening alloy, with a typical heat treatment consisting of solution annealing before a two-stage ageing process. Depending on the heat treatment procedure, strength or ductility can be enhanced, typically at the cost of the other. This study aims to determine a heat treatment procedure suitable for applications that require high ductility. Tensile tests of Inconel 718 processed by laser powder bed fusion additive manufacturing has been carried out on specimens subjected to different heat treatment procedures. The results show that solution annealing above 1010 °C followed by a two-stage ageing at 720 °C/8 h with furnace cooling to 620 °C/2 h and final holding at 620 °C/10 h, produce elongation at break of above 30% tested at room temperature and above 24% tested at 650 °C.